- Model NO.: lh903540
- Material: Silicone Rubber
- Form: Liquid Rubber
- Mixing Ratio: 10:1
- Cure Time: 3-5seconds in 150degrees
- Trademark: Lianhuan Group
- Origin: Shenzhen, China
- Raw Material: Silicone Rubber
- Appearance: Fluid Liquid
- Color: Translucent,White,Black,Any Color Required
- Open Time: 2-3days
- Product Name: Screen Printing Ink for Textile Print/Swimming Cap
- Transport Package: 5kg/Drum, 25kg/Drum, 200kg/Drum
- HS Code: 3910000000
screen printing Ink for textile print/swimming cap wristband
Silicone ink Appliation                                                 :
Suitable for most natural and synthetic fabrics, including elastic fabric
  Jerseys
  Hats & caps
   Sweaters
  Jackets
  Gloves
   Sleepwear
   Pants & shorts
  Bathing suits
   Undergarments
  Uniforms
  Shirts
  Sweatshirts
Silicone Ink features                                                  :
 Good hand feel: Soft, non-sticky handle with no blocking problem upon folding
  Excellent durability: Wash- and weather-resistance
  Color fastness: No color migration, even between red and white
 Improved fashion appearance: Semi-gloss finish with no creasing
  High elongation: Suitable for fabric with Lycra content
  Fast cure: Skin cures in 3 to 6 seconds at skin temperatures between 100-130°C
  Operation-friendly: Suitable viscosity and thixotropy for manual screen printing
 Easily pigmented: A base gel / catalyst system of less than 10 percent
  Environmentally sound: Does not contain organotin, phthalate, formaldehyde, PVC or solvent
  Reduced total cost of use: Lower process time and better coverage
  Low shrinkage(<0.1%) Â
 Excellent performance of anti-slip
  Good skid-proof effect and high adhesive strength
 Wearproof, wash-resistant, high temperature resistant
  Non-toxic and odorless, food grade silicone
 High transparency and good tear-strength
 Wearproof, washable, high temperature resistance
 Three-dimensional level
Â
Silicone Ink Datasheet                                 :
Model |
901040 |
903540 |
Appearance |
Transparent |
Transparent |
Hardness(shore A) |
35±2 |
42±2 |
Mix ratio(A:B) |
10:1 |
10:1 |
Viscosity(mPa.s) |
60000~100000 |
300000~380000 |
Tensile strength(Mpa) |
4.6 |
4.8 |
Tear-strength(KN/m) |
20±2 |
22±2 |
Elongation(%) |
450 |
420 |
Pot life/working time(25degree) |
2-3Â hours |
2-3Â hours |
curing time(125degree) |
30~50Â seconds |
30~50Â seconds |
 (ps: the hardness and viscosity is adjustable)
Â
Silicone Ink Prepare Methods                                  :
Mixed Color master batch: Using it when needing various colors.
For ink to be yellow: first change base A part to white color (10%) white pigment in. then mixed with yellow color paste1% to colors!Â
Same process as for ink to blue and Red ink!
For ink to be black :Â add 5% of black color paste to base A part mixed well.
For ink to be grey:Â add 3% of black color paste and 5% of white color paste to base A part mixed well
Silicone Ink Mix process                                          :
1.  Mixed 10% CATATLYST curing agent B Part into small amount of silicone ink A Part(90%).Â
2.  The curing agent should be mixed very well, Otherwise,some parts won't be cured.
3.  could use thinner for decrease the viscosity,over 15% of thinner, the abrasiveness, durability and adhesion force will be reduce. There tested before production is required.
Silicone Ink Drying Methods                                      :
1. According to different thickness of silicone ink, the curing time is different. Normal situation for mixing Part A: Part B =10:1 curing time is 50seconds with the temperature of 150degree (polyaddition process).Â
2. When the room temperature is above 25degree (humidity 50%), room temperature cure can be carried out under summer condition
3.Color master batch: Using it when needing various colors.
Â
Â
Scouring Pad,Industrial Scouring Pad,Nylon Abrasive Scouring Pad,Scouring Pad For Polishing